1-1. Alkyl Dimethyl Benzyl Ammonium chlorides
|
Product Name |
Alkyl Group |
Application |
|
Non-emulsion
Types |
L-518
L-533
L-540 |
Pigment dispersing agent for plastic high concentrate (master batch), External lubricant for PVC extrusion processing, Wear resistance improver of paints and inks, Engineering plastic lubricants, Hot-melt processability improver, paper coating agent, rubber processability improver, Improver of various waxes' fusion point. |
|
H-633
H-640 |
Dispersing agent of PS retardants and plastic pigment concentrates (master batch), Wear resistance improver of paints and inks, Engineering plastic lubricants, Hot-melt processability improver, paper coating agent, EPS nucleating agent, Improver of various waxes' fusion point. |
|
LH-1200 |
Pigment dispersing agent for high concentrate (master batch) |
|
LH-400
HCF-440 |
Jelly compounds for cables |
|
HLP-300P
HLP-300F |
PVC internal lubricants, Calpeat processing agents, Hot-melt processing agents Pigment dispersing agent, for plastic pigment concentrates (master batch), Improver of various waxes' fusion point, PVC internal lubricants, Wear resistance improver of paint improver for road signal |
|
Emulsion
Types |
LE-718
LE-705 |
Fabric softners, floor varnishes, PVC extrusion processing internal lubricants Protector of paint sedimentation. |
1-2. Homo-Polymers
|
Item |
Softening
Point
(°C) |
Melt viscosity
(@140°C, cPs) |
Density
(@25°C), g/cm3) |
Penetration hardness
(0.1mm) |
Acid value
(mgKOH/g) |
Physical forms |
|
L - 518 |
101±3 |
180±50 |
0.92±0.01 |
max 3.5 |
Nil |
Power |
|
L -533 |
106±3 |
300±100 |
0.92±0.01 |
max 3.5 |
Nil |
Power |
|
L - 540 |
107±3 |
400±100 |
0.92±0.01 |
max 3.0 |
Nil |
Power |
|
L -570 |
108±3 |
750±100 |
0.92±0.01 |
max 3.0 |
Nil |
Power |
|
L - 633 |
118±3 |
330±100 |
0.93±0.02 |
max 2.0 |
Nil |
Power |
|
H - 640 |
120±3 |
400±100 |
0.96±0.02 |
max 2.0 |
Nil |
Power |
|
LH - 1200 |
109±3 |
1,100±150 |
0.92±0.01 |
max 3.5 |
Nil |
Power |
|
LCF - 400 |
108±3 |
500±100 |
0.92±0.01 |
max 3.5 |
Nil |
Power |
|
HCF - 440 |
118±2 |
650±50 |
0.94±0.01 |
max 1.0 |
Nil |
Power |
|
HLP - 300P |
110±10 |
50±20 |
0.94±0.01 |
max 9.0 |
Nil |
Power |
|
HLP - 300F |
110±10 |
10 ~ 100 |
0.94±0.01 |
max 9.0 |
Nil |
Flakes |
1-3. Oxidized Homo-Polymers / Emulsifiable Type
|
Item |
Softening
Point
(°C) |
Melt viscosity
(@140°C, cPs) |
Density
(@25°C), g/cm3) |
Penetration hardness
(0.1mm) |
Acid value
(mgKOH/g) |
Physical forms |
|
LE- 718 |
100 3 |
250 100 |
0.94±0.01 |
max 4.5 |
16±2 |
Power |
|
LE- 705 |
110 10 |
50 20 |
0.94±0.01 |
max 6.5 |
16±2 |
Power |
2-1. PP Wax (Polypropylene wax)
|
Product Name |
Alkyl Group |
Application |
|
Non-emulsion
Types |
PH-820
PC-820
PH-810
PC-820 |
Pigment dispersing agent for high concentrate (master batch) Improver of hot-melt processability, Improver of grease fusion point |
|
Oxidization Types |
PHE-920
PCE-903 |
Processability improver of hot-melt, Battery fillers |
2-2. Homo-Polymers
|
Item |
Softening
Point
(°C) |
Melt viscosity
(@170°C, cPs) |
Density
(@25°C), g/cm3) |
Penetration hardness
(0.1mm) |
Acid value
(mgKOH/g) |
Physical forms |
|
PH-820 |
158±3 |
200±100 |
0.89±0.01 |
max 1.0 |
Nil |
Power |
|
PH-810 |
158±3 |
90±50 |
0.89±0.01 |
max 1.0 |
Nil |
Power |
2-3. Co-Polymers
|
Item |
Softening
Point
(°C) |
Melt viscosity
(@140°C, cPs) |
Density
(@25°C), g/cm3) |
Penetration hardness
(0.1mm) |
Acid value
(mgKOH/g) |
Physical forms |
|
PC-820 |
148±3 |
200±100 |
0.89±0.01 |
max 1.0 |
Nil |
Power |
|
PC-810 |
148±3 |
90±50 |
0.89±0.01 |
max 1.0 |
Nil |
Power |
2-4. Oxidized Polypropylenes / Emalsifiable type
|
Item |
Softening
Point
(°C) |
Melt viscosity
(@140°C, cPs) |
Density
(@25°C), g/cm3) |
Penetration hardness
(0.1mm) |
Acid value
(mgKOH/g) |
Physical forms |
|
PHE-920 |
158±3 |
200±50 |
0.89±0.01 |
max 1.0 |
4 |
Lumps |
|
PCE-903 |
120±3 |
50±10 |
0.89±0.01 |
max 30 |
4 |
Lumps |
|
|
|
|
| |
|
|
|